CIGS-perovskite tandem cell achieves record efficiency of 25.5 %
The tandem solar cell shown here combines CIGSe and perovskite semiconductors. It is slightly larger than 1 square centimeter and achieves a record efficiency of 25.5% for this combination of materials. © G. Farias Basulto / HZB
A Berlin-based team from HZB and Center for the Science of Materials Berlin (CSMB) at the Humboldt-Universität zu Berlin has set a new record for a tandem solar cell. Using a combination of a CIGS semiconductor layer and perovskite, along with several optimised intermediate layers, they were able to convert 25.5% of sunlight into electrical energy. The previous record for this combination of materials and this size of cell stood at 24.6%. The new record has been certified and is visible in the prestigious Solar Cell Efficiency Tables (the "Green Tables"), which serve as the definitive ledger for the global photovoltaic community.
To be included in this special ‘record table’, not only is a high efficiency required, but also an area of more than 1 cm2. The well-known NLR-table (formerly NREL), by contrast, only lists the maximum efficiency per technology, even if the cell has an area of 0.001 cm2.
'To push past our previous milestone within the framework of the European project SOLMATES, we employed CIGSe-bottom cells with different band gaps (i.e. 1.05 eV and 1.1 eV) and two different thicknesses of aluminium doped zink oxides with similar characteristics. We also tested different cell architectures, added to the continuous improvements we had achieved with our previous record,' says Dr. Guillermo Farias Basulto.
By aiming to reduce interfacial recombination losses and improve device stability, chemist Wuai Zhang screened multiple combinations of nickel oxide (NiOx) and self-assembled monolayers (SAMs) as hole transport material. Zhang also refined the electron-selective contact processing by regulating the initial thermal evaporation rate of Buckminsterfullerene (C60) onto an ultra-thin (1 nm) lithium fluoride (LiF) passivation layer.
The cell has an area of 1.081 cm2, which, of course, is still small. However, within the SOLMATES project, Nicolas Otto from the University of applied sciences in Berlin (HTW) together with Thede Mehlhop from HZB were able to able to fabricate a mini- module with a similar stack of materials with about 19.7 % efficiency with an area of 2.25cm2.
‘The physics embedded in our current cell architecture suggests that 25.5% is merely a steppingstone, given that our in-house testing of similar architectures have already reached efficiencies of 27.5%’, Farias-Basulto points out.
- 3D magnetic field experiment at BESSY II takes spintronics a step further(Fe0.63Ni0.3Pd0.07)3P or FNPP is a magnetic material that exhibits complex magnetic structures even at room temperature. This makes the material of interest for spintronics, a field that could enable data processing with significantly lower energy consumption. One potential application is novel magnetic memory devices. However, generating and modifying the desired structures in a controlled manner remains a challenge to date. A new study led by HZB has now taken a step forward in this regard. They demonstrated at the worldwide unique VEKMAG-Station at BESSY II, that a tiny external B-field in the plane of the magnetic patterns is sufficient to change them.
- Thin nickel films boost green hydrogen productionUltra-thin nickel oxide coatings can significantly improve the performance of anion exchange membrane (AEM) water electrolysers, a promising technology for producing green hydrogen. This was demonstrated by a team led by HZB scientist Dr. Michelle Browne. The results show that a nickel oxide film only 10 nanometres thick outperformed conventional nickel oxide powder electrodes while using less than 1% of the catalyst material. The study is published in the Journal of Materials Chemistry A,
- Detailed insights at BESSY II into the oxidation processes of copperBefore pure copper oxide builds up, complex superstructures such as ‘29’CuxO, are formed. The new results on the '29' CuxO superstructure have relevance for catalyst research and corrosion protection in the development of safe copper containers for nuclear waste repositories.