Raghuwanshi, V.S.; Tatchev, D.; Haas, S.; Harizanova, R.; Gugov, I.; Rüssel, C.; Hoell, A.: Structural analysis of magnetic nanocrystals embedded in silicate glasses by anomalous small-angle X-ray scattering. Journal of Applied Crystallography 45 (2012), p. 644 - 651
10.1107/S002188981202064X
Abstract:
The present work reports the structural analysis of magnetic nanocrystals of Fe- and Mn-containing phases formed during annealing of the glass 13.6Na2O-62.9SiO2-8.5MnO-15.0Fe2O3-x (mol%) at 823 K for different periods of time. X-ray diffraction investigation shows the formation of a mixture of MnFe2O4 and Fe3O4 phases. Furthermore, small-angle X-ray scattering and anomalous small-angle X-ray scattering (ASAXS) experiments were used to extract quantitative information about the structure of the formed nano-sized crystals, as well as their phase compositions, volume fractions and size distributions. ASAXS analysis reveals the formation of spherical core-shell particles with the size of the particles between 10 and 50 nm. The concentrations of iron atoms in the core are higher than those in the shell and in the remaining matrix. With increasing annealing time, the ratio of Mn to Fe increases in the nanoparticles and the crystalline phase moves toward the pure jacobsite phase. Evaluated compositions reveal the presence of SiO2 in the shell. This shell acts as a diffusion barrier for the nanocrystal-forming ions, and the growth of the particles is kinetically constrained.