Nie, M.; Ellmer, K.: Morphology and structure evolution of Cu(In,Ga)S2 films deposited by reactive magnetron co-sputtering with electron cyclotron resonance plasma assistance. Journal of Applied Physics 115 (2014), p. 084902/1-8
10.1063/1.4866717
Abstract:
Cu(In,Ga)S2 films were deposited on Mo coated soda lime glass substrates using an electron cyclotron resonance plasma enhanced one-step reactive magnetron co-sputtering process (ECR-RMS). The crystalline quality and the morphology of the Cu(In,Ga)S2 films were investigated by X-ray diffraction, atomic force microscopy, scanning electron microscopy and X-ray fluorescence. We also compared these CIGS films with films previously prepared without ECR assistance and find that the crystallinity of the CIGS films is correlated with the roughness evolution during deposition. Atomic force microscopy was used to measure the surface topography and to derive one-dimensional power spectral densities (1DPSD). All 1DPSD spectra of CIGS films exhibit no characteristic peak which is typical for the scaling of a self-affine surface. The growth exponent β, characterizing the roughness Rq evolution during the film growth as Rq- dfβ , changes with film thickness. The root-mean-square roughness at low temperatures increases only slightly with a growth exponent β = 0.013 in the initial growth stage, while Rq increases with a much higher exponent β = 0.584 when the film thickness is larger than about 270 nm. Additionally, we found that the H2S content of the sputtering atmosphere and the Cu- to-(In+Ga) ratio has a strong influence of the morphology of the CIGS films in this one-step ECR-RMS process.