• Li, J.; Dobrovolsky, A.; Merdasa, A.; Unger, E.L.; Scheblykin, I.G.: Luminescent Intermediates and Humidity-Dependent Room-Temperature Conversion of the MAPbI3 Perovskite Precursor. ACS Omega 3 (2018), p. 14494-14502

10.1021/acsomega.8b01799
Open Access Version

Abstract:
Preparation of metal-halide perovskites under room temperature attracts attention because of energy saving by removing thermal annealing. Room-temperature trans- formation of spin-cast wet films consisting of methylammo- nium (MA) iodide, PbI2, and dimethylformamide toward solid MAPbI3 perovskite proceeds via several intermediate crystal- line states and is strongly dependent on ambient humidity. Light transmission and photoluminescence (PL) microscopy and spectroscopy were used to monitor the growth of crystals and transformation of their properties in time under nitrogen atmosphere at room temperature. Under low humidity, a highly luminescent intermediate phase with low absorption in the visible range appears, with the PL spectra composed of several bands in the range from 600 to 760 nm. We assign these bands to low-dimensional (nanocrystals and two-dimensional inclusions) MAPbI3 intermediates, where the exciton confinement shifts the spectrum to higher energies in comparison with the bulk MAPbI3. The intermediate levels of ambient humidity (10−50%) appear to catalyze the conversion of the intermediate phase to MAPbI3. At a high ambient humidity (>80%), the initially formed MAPbI3 is quickly transformed to the transparent hydrate phase of MAPbI3. The role of ambient water catalyzing the material transformation by competing for Pb coordination with the solvent molecules is discussed.