Batman lights the way to compact data storage

<span class="imageCaption">Researchers at PSI spotted a curious black-and-white magnetic substructure on a five-by-five micrometre square &ndash; and were reminded of the stylised Batman logo. The black areas reveal where the magnetisation is pointing downwards, i.e. into the picture; the white ones where it is pointing upwards. <br /></span>

Researchers at PSI spotted a curious black-and-white magnetic substructure on a five-by-five micrometre square – and were reminded of the stylised Batman logo. The black areas reveal where the magnetisation is pointing downwards, i.e. into the picture; the white ones where it is pointing upwards.
© PSI

Researchers at the Paul Scherrer Institute (PSI) have succeeded in switching tiny, magnetic structures using laser light and tracking the change over time. In the process, a nanometre-sized area bizarrely reminiscent of the Batman logo appeared. The research results could render data storage on hard drives faster, more compact and more efficient.

Excerpt of the PSI-Press release:

The researchers at PSI teamed up with colleagues from the Netherlands, Germany and Japan for the project. Two years ago, the international research team already succeeded in demonstrating that a short, intensive laser pulse can switch micro-magnets hundreds of times faster than a magnetic head. And the laser is lower in energy and thus more cost-effective, too. The trick evidently lies in the fact that the laser light heats up the tiny magnets very quickly and is thus able to convert them into the other state. “Using light for magnetic switching clearly works. But why exactly it does is still the subject of debate in the research community,” explains Frithjof Nolting, the lab head on the PSI study.

“This could be the way to store even more data on even smaller hard drives one day,” says Loïc Le Guyader, who was also involved in the PSI experiments, and is now working at the Helmholtz-Zentrum Berlin.


Please read the complete press release here:

http://www.psi.ch/media/batman-lights-the-way-to-compact-data-storage

Publication: Nanoscale sub-100 picosecond all-optical magnetization switching in GdFeCo microstructures.
L. Le Guyader, M. Savoini, S. El Moussaoui, M. Buzzi, A. Tsukamoto, A. Itoh, A. Kirilyuk, T. Rasing, A.V. Kimel and F. Nolting,
Nature Communications, 12 January 2014,
DOI: 10.1038/ncomms6839

Laura Hennemann /PSI

  • Copy link

You might also be interested in

  • Green hydrogen: MXenes shows talent as catalyst for oxygen evolution
    Science Highlight
    09.09.2024
    Green hydrogen: MXenes shows talent as catalyst for oxygen evolution
    The MXene class of materials has many talents. An international team led by HZB chemist Michelle Browne has now demonstrated that MXenes, properly functionalised, are excellent catalysts for the oxygen evolution reaction in electrolytic water splitting. They are more stable and efficient than the best metal oxide catalysts currently available. The team is now extensively characterising these MXene catalysts for water splitting at the Berlin X-ray source BESSY II and Soleil Synchrotron in France.
  • "BESSY is of immense importance for Berlin"
    News
    02.09.2024
    "BESSY is of immense importance for Berlin"
    At the end of August, the Senator for Research, Health, and Long-Term Care, Dr Ina Czyborra, together with the State Secretary for Science, Dr Henry Marx, ended her summer tour with a visit to HZB in Adlershof. She publicly declared her political support for the new construction of BESSY III.

  • Langbeinites show talents as 3D quantum spin liquids
    Science Highlight
    23.08.2024
    Langbeinites show talents as 3D quantum spin liquids
    A 3D quantum spin liquid has been discovered in the vicinity of a member of the langbeinite family. The material's specific crystalline structure and the resulting magnetic interactions induce an unusual behaviour that can be traced back to an island of liquidity. An international team has made this discovery with experiments at the ISIS neutron source and theoretical modelling on a nickel-langbeinite sample.