Zhao, J.; Su, Z.; Pascual, J.; Wu, H.; Wang, H.; Aldamasy, M.H.; Zhou, Z.; Wang, C.; Li, G.; Li, Z.; Gao, X.; Hsu, C.S.; Li, M.: Suppressed Defects by Functional Thermally Cross-Linked Fullerene for High-Efficiency Tin-Lead Perovskite Solar Cells. Advanced Materials 36 (2024), p. 2406246/1-8
10.1002/adma.202406246
Open Access Version
Abstract:
Mixed tin-lead (Sn-Pb) perovskites have attracted the attention of the community due to their narrow bandgap, ideal for photovoltaic applications, especially tandem solar cells. However, the oxidation and rapid crystallization of Sn2+ and the interfacial traps hinder their development. Here, cross-linkable [6,6]-phenyl-C61-butyric styryl dendron ester (C-PCBSD) is introduced during the quenching step of perovskite thin film processing to suppress the generation of surface defects at the electron transport layer interface and improve the bulk crystallinity. The C-PCBSD has strong coordination ability with Sn2+ and Pb2+ perovskite precursors, which retards the crystallization process, suppresses the oxidation of Sn2+, and improves the perovskite bulk and surface crystallinity, yielding films with reduced nonradiative recombination and enhanced interface charge extraction. Besides, the C-PCBSD network deposited on the perovskite surface displays superior hydrophobicity and oxygen resistance. Consequently, the devices with C-PCBSD obtain PCEs of up to 23.4% and retained 97% of initial efficiency after 2000 h of storage in a N2 atmosphere.