Charge Order competes with superconductivity
Stripe order of charge carriers in Bi2Sr2CaCu2O8+x [2]. The figure shows the structure with a period of approximately one nanometer (front) and the related diffraction pattern (back) obtained by a so-called Fourier transformation (Yazdani Lab, Princeton University).
Today in Science Express: Charge carriers in cuprate high-Tc superconductors form nanostripes that suppress superconductivity, as shown by guest researchers from Princeton and Vancouver using synchrotron radiation at BESSY II
Superconductors are materials that can conduct electricity without any loss of energy. In order to exhibit this property, however, classical superconductors need to be cooled almost to absolute zero (minus 273 degrees centigrade). Even the so-called high-Tc superconductors still require very low temperatures of minus 200 degrees centigrade. While cooling down to these temperatures involves substantial effort, superconductors are already employed in many areas, e.g., for magnetic resonance tomography in medical applications. Despite extensive research, materials providing lossless conduction of electricity at room temperature are missing up to now.
High-Tc superconductors were discovered in 1986, the Nobel prize for the discovery came only one year later. The phenomenon of superconductivity at high temperatures is found in a class of materials called the cuprates, complex compounds of copper and oxygen, and additional ingredients. They are in the focus of research for almost 30 years now. Many aspects of the high-Tc cuprates, however, are still to be understood. This is due to the subtle details determining the properties of the charge carriers in these materials. Thus, a number of competing mechanisms preclude the superconducting state.
One of the competing states of the materials is a regular stripe pattern of charge carriers on the nanoscale. This kind of order freezes the charge carriers and prevents superconductivity. Already last year, guest researchers at BESSY II could elucidate the importance of this mechanism and its connection with superconductivity in a representative group of cuprates [1]. Lead by two research groups from Princeton and Vancouver, international teams of scientists have now identified the so-called charge order as a generic property of this class of materials.
For their research, they used the XUV diffractometer developed at HZB, which is operated at the UE46_PGM1 beamline at BESSY II. Employing soft x-ray synchrotron radiation, they succeeded in detecting the elusive phenomenon of charge order and measured the related nanostructures with high precision. This is an important step towards understanding the charge order and its connection to superconductivity in the cuprates. The research was conducted in close cooperation with scientists from the Department Quantum Phenomena in Novel Materials (previously from the Institute of Complex Magnetic Materials) at HZB. The results are now published in two articles in Science [2,3]. “Identifying and understanding the mechanisms competing with superconductivity raise the hope to control and eventually deactivate them. This may be one step towards superconductivity at room temperature”, explains Dr. Eugen Weschke, who supervised the experiment at BESSY II.
[1] G. Ghiringelli et al., Long-Range Incommensurate Charge Fluctuations in (Y,Nd)Ba2Cu3O6+x, Science 337, 821 (2012).
[2] Eduardo H. da Silva Neto et al., Ubiquitous Interplay between Charge Ordering and High-Temperature Superconductivity in Cuprates, Science 2013. DOI: 10.1126/science.1243479
[3] R. Comin et al., Charge order driven by Fermi-arc instability in Bi2Sr2−xLaxCuO6+δ, Science (2013). DOI: 10.1126/science.1242996
- Energy of charge carrier pairs in cuprate compoundsHigh-temperature superconductivity is still not fully understood. Now, an international research team at BESSY II has measured the energy of charge carrier pairs in undoped La₂CuO₄. Their findings revealed that the interaction energies within the potentially superconducting copper oxide layers are significantly lower than those in the insulating lanthanum oxide layers. These results contribute to a better understanding of high-temperature superconductivity and could also be relevant for research into other functional materials.
- Electrocatalysis with dual functionality – an overviewHybrid electrocatalysts can produce green hydrogen, for example, and valuable organic compounds simultaneously. This promises economically viable applications. However, the complex catalytic reactions involved in producing organic compounds are not yet fully understood. Modern X-ray methods at synchrotron sources such as BESSY II, enable catalyst materials and the reactions occurring on their surfaces to be analysed in real time, in situ and under real operating conditions. This provides insights that can be used for targeted optimisation. A team has now published an overview of the current state of knowledge in Nature Reviews Chemistry.
- BESSY II: Phosphorus chains – a 1D material with 1D electronic propertiesFor the first time, a team at BESSY II has succeeded in demonstrating the one-dimensional electronic properties in phosphorus. The samples consisted of short chains of phosphorus atoms that self-organise at specific angles on a silver substrate. Through sophisticated analysis, the team was able to disentangle the contributions of these differently aligned chains. This revealed that the electronic properties of each chain are indeed one-dimensional. Calculations predict an exciting phase transition to be expected as soon as these chains are more closely packed. While material consisting of individual chains with longer distances is semiconducting, a very dense chain structure would be metallic.