Perovskite solar cells: Defects trap charge carriers - and release them again
Five different types of defects in MAPI-perovskites were examined and characterised. The result: a large proportion of defects is not trapping the charge carriers for long. © HZB
An international team at HZB and Charles University Prague has investigated how charge carriers in so called MAPI-perovskite semiconductors interact with different defects. They show that a large proportion of defects quickly releases trapped charge carriers. These results could help to further improve the properties of perovskite solar cells.
Among the most exciting materials for solar cells are the so-called MAPI semiconductors. They consist of organic methylammonium cations and lead iodide octahedra that form a perovskite structure. MAPI based solar cells have achieved efficiencies of 25 % within a few years. But so far, the semi-organic semiconductors are still ageing rapidly.
Now, for the first time, physicists at HZB, CNRS, France and Charles University, Prague, Czech Republik, have precisely characterised five different defect types and measured the interaction between these defects and the charge carriers.
Using a combination of highly sensitive spectroscopy methods, they succeeded in experimentally determining the concentration, energy, capture cross-section and charge capture time of the different defects and creating a map of the defects. By using electric pulses, they made sure that the measurements did not affect the quality of the material.
The measurement results allow the reliable differentiation between electron and hole transport and the determination of their most important parameters: Mobilities, lifetimes and diffusion lengths. "This work thus provides answers to questions that have been discussed for a long time in the field of perovskite solar cells," says Dr. Artem Musiienko, first author of the publication and postdoc at HZB.
An important finding: a large proportion of the defects release the captured charge carriers again after a short time. "This may partly explain these particularly high efficiencies of the MAPI perovskites," says Musiienko. These results pave the way to optimise MAPI perovskites in terms of defect concentration, combining high efficiencies with good stability.
- Two Humboldt-Fellows join HZBIn 2024, two young scientists joined HZB as Humboldt Fellows. Kazuki Morita joined Prof. Antonio Abate's group and brings his expertise in modelling and data analysis to solar energy research. Qingping Wu is an expert in battery research and works with Prof. Yan Lu on high energy density lithium metal batteries.
- Less is more: Why an economical Iridium catalyst works so wellIridium-based catalysts are needed to produce hydrogen using water electrolysis. Now, a team at HZB has shown that the newly developed P2X catalyst, which requires only a quarter of the Iridium, is as efficient and stable over time as the best commercial catalyst. Measurements at BESSY II have now revealed how the special chemical environment in the P2X catalyst during electrolysis promotes the oxygen evolution reaction during water splitting.
- 20 years of promoting science in the school lab38,000 visitors in 20 years: high demand shows need for science education
Twenty years ago, on 29 November 2004, Klaus Böger, then Senator for Education in Berlin, opened one of the capital's first school laboratories. Since then, Helmholtz-Zentrum Berlin (HZB), in cooperation with the Berlin Senate, has successfully promoted science education through project days and further training in the school lab.