A simpler way to inorganic perovskite solar cells

Under the scanning electron microscope, the CsPbI<sub>3</sub> layer (large blocks in the upper part of the image) on the FTO substrate looks almost exactly the same after annealing in ambient air as after annealing under controlled conditions.

Under the scanning electron microscope, the CsPbI3 layer (large blocks in the upper part of the image) on the FTO substrate looks almost exactly the same after annealing in ambient air as after annealing under controlled conditions. © HZB

Die Box-Chart-Statistik zeigt Wirkungsgrade von Solarzellen, die unter kontrollierten Bedingungen hergestellt wurden im Vergleich mit Solarzellen, die in Umgebungsluft gegl&uuml;ht wurden. &nbsp;

Die Box-Chart-Statistik zeigt Wirkungsgrade von Solarzellen, die unter kontrollierten Bedingungen hergestellt wurden im Vergleich mit Solarzellen, die in Umgebungsluft geglüht wurden.   © HZB

Inorganic perovskite solar cells made of CsPbI3 are stable over the long term and achieve good efficiencies. A team led by Prof. Antonio Abate has now analysed surfaces and interfaces of CsPbI3 films, produced under different conditions, at BESSY II. The results show that annealing in ambient air does not have an adverse effect on the optoelectronic properties of the semiconductor film, but actually results in fewer defects. This could further simplify the mass production of inorganic perovskite solar cells.

Metal halide perovskites have optoelectronic properties that are ideally suited for photovoltaics and optoelectronics. When they were discovered in 2009, halide perovskites in solar cells achieved an efficiency of 3.9 per cent, which then increased extremely fast. Today, the best perovskite solar cells achieve efficiencies of more than 26 per cent. However, the best perovskite semiconductors contain organic cations such as methylammonium, which cannot tolerate high temperatures and humidity, so their long-term stability is still a challenge. However, methylammonium can be replaced by inorganic cations such as Cesium (Cs). Inorganic halide perovskites with the molecular formula CsPbX3 (where X stands for a halide such as chloride, bromide and iodide) remain stable even at temperatures above 300 °C. CsPbI3 has the best optical properties for photovoltaics (band gap 1.7 eV).

Production in glove boxes

Perovskite semiconductors are produced by spin coating or printing from a solution onto a substrate and are typically processed in glove boxes under a controlled atmosphere: There, the solvent is evaporated by heating, after which a thin layer of perovskite crystallizes. This 'controlled environment' significantly increases the cost and complexity of production.

...or ambient conditions

In fact, CsPbI3 layers can also be annealed under ambient conditions without loss or even with an increase in efficiency of up to 19.8 per cent, which is even better than samples annealed under controlled conditions.

What happens at the interfaces?

"We investigated the interfaces between CsPbI3 and the adjacent material in detail using a range of methods, from scanning electron microscopy to photoluminescence techniques and photoemission spectroscopy at BESSY II," says Dr. Zafar Iqbal, first author and postdoctoral researcher in Antonio Abate's team.

BESSY II unveils a surface modification

At BESSY II, the team of Prof. Marcus Bär used hard X-ray photoelectron spectroscopy (HAXPES) to analyse the chemical and electronic structure of the differently annealed CsPbI3 and perovskite/hole transport layer interfaces. "In the samples that were annealed in ambient air, we observed a surface modification that improves the mobility of the charge carriers at the interface," explains Iqbal. Optical spectroscopy showed that annealing in air resulted in fewer defects.

Upscaling might become simpler

"Our study explains why the annealing of CsPbI3 films in ambient air works well," says Iqbal. This could be particularly interesting for upscaling processes for potential mass production.

Note: Zafar Iqbal was financed by a fellowship by Deutscher Akademischer Austauschdienst (DAAD) during his PhD in the Abate Group.

arö

  • Copy link

You might also be interested in

  • Ultrafast dissociation of molecules studied at BESSY II
    Science Highlight
    02.12.2024
    Ultrafast dissociation of molecules studied at BESSY II
    For the first time, an international team has tracked at BESSY II how heavy molecules – in this case bromochloromethane – disintegrate into smaller fragments when they absorb X-ray light. Using a newly developed analytical method, they were able to visualise the ultrafast dynamics of this process. In this process, the X-ray photons trigger a "molecular catapult effect": light atomic groups are ejected first, similar to projectiles fired from a catapult, while the heavier atoms - bromine and chlorine - separate more slowly.
  • 20 years of promoting science in the school lab
    News
    29.11.2024
    20 years of promoting science in the school lab
    38,000 visitors in 20 years: high demand shows need for science education

    Twenty years ago, on 29 November 2004, Klaus Böger, then Senator for Education in Berlin, opened one of the capital's first school laboratories. Since then, Helmholtz-Zentrum Berlin (HZB), in cooperation with the Berlin Senate, has successfully promoted science education through project days and further training in the school lab.

  • Battery research with the HZB X-ray microscope
    Science Highlight
    18.11.2024
    Battery research with the HZB X-ray microscope
    New cathode materials are being developed to further increase the capacity of lithium batteries. Multilayer lithium-rich transition metal oxides (LRTMOs) offer particularly high energy density. However, their capacity decreases with each charging cycle due to structural and chemical changes. Using X-ray methods at BESSY II, teams from several Chinese research institutions have now investigated these changes for the first time with highest precision: at the unique X-ray microscope, they were able to observe morphological and structural developments on the nanometre scale and also clarify chemical changes.