BESSY II: New procedure for better thermoplastics
In nano-IR imaging, the layer structures of the pure PVDF/PLLA mixture (left) and with the SAD additive (right) are clearly distinguishable. The light and dark colours correspond to the PLLA and PVDF phases, respectively. When SAD is added, the domain sizes of the two phases are reduced. © TU Eindhoven/HZB
During beamtime at BESSY II: Claudia Hanegraaf, Paul van Heugten and Hamid Ahmadi, TU Eindhoven, NL (from left to right). © TU Eindhoven/HZB
Bio-based thermoplastics are produced from renewable organic materials and can be recycled after use. Their resilience can be improved by blending bio-based thermoplastics with other thermoplastics. However, the interface between the materials in these blends sometimes requires enhancement to achieve optimal properties. A team from the Eindhoven University of Technology in the Netherlands has now investigated at BESSY II how a new process enables thermoplastic blends with a high interfacial strength to be made from two base materials: Images taken at the new nano station of the IRIS beamline showed that nanocrystalline layers form during the process, which increase material performance.
Bio-based thermoplastics are considered environmentally friendly, as they are sourced from non-petroleum-based raw materials and can be recycled just like standard thermoplastics. A thermoplastic base material is Polylactic acid (PLA), which can be produced from sugar cane or corn. Researchers around the world are working to optimise the properties of PLA-based plastics, for example by mixing them with other thermoplastic base materials. However, this is a real challenge.
A new process for better blends
Now, a team from the TU Eindhoven led by Prof. Ruth Cardinaels is showing how PLA can be successfully mixed with another thermoplastic. They developed a process in which certain PLA-based copolymers (e.g. SAD) are formed during production, which facilitate the mixing of the two raw materials by forming particularly stable (stereo)-crystalline layers at the interfaces between the different polymer phases (ICIC strategy).
Insights at the IRIS-Beamline
At BESSY II, they have now discovered which processes ensure that the mechanical properties of the mixed thermoplastic are significantly better. To do so, they examined pure 50% blends of the thermoplastics PLA and polyvinylidene fluoride (PVDF) as well as samples with the PLA-based copolymers at the IRIS beamline of BESSY II.
Stereocomplex crystals at the interfaces
Using infrared spectroscopy on the IRIS beamline, PhD student Hamid Ahmadi was able to demonstrate the formation of the PLA-based copolymer SAD. Further X-ray measurements showed how the formation of SAD affects the crystallisation behaviour. The new nano imaging and spectroscopy capabilities at the IRIS beamline allow for advanced chemical visualization and identification from sample areas as small as 30 nm. This precision was crucial in determining that the stereocomplex crystals are exclusively located at the interface. Infrared nanoscopy images showed a 200–300 nm thick layer of stereocomplex crystals at the interfaces.
Reason for more stability
The formation of stereocomplex crystals at the interfaces increases the stability and crystallisation temperature. Nucleation at the interface accelerates the overall crystallisation process within the PLLA/PVDF blend. In addition, the interfacial crystalline layer improves the transfer of mechanical stresses between the phases and thus the tensile properties; the elongation at break even increases by up to 250 %.
“By elucidating the location and distribution of the crystalline layer in our samples, we could understand the procedure of mixing much better”, Hamid Ahmadi says. “By developing a new strategy we have cleared a path for the development of high-performance polymer blends”, Ruth Cardinaels adds.
Note: The IRIS beamline at BESSY II was extended by a nanomicroscopy facility in 2024, which makes it possible to create images of sample areas of ~30 nm and to carry out IR spectroscopy. You can read more about this in the news about the IRIS beamline dated 25 April 2024.
- Israel Ibukun Olaniyan receives the Helmholtz Doctoral Award 2026At Helmholtz, more than 8,000 doctoral candidates conduct research. Eleven of them have now been honored for their original and outstanding work, among them Dr Israel Ibukun Olaniyan from the HZB. His doctoral thesis "Ferroelectricity at the nanoscale in epitaxial BaTiO3 on silicon" in the group of Professor Catherine Dubourdieu represents a step towards a new nanoelectronics based on topological defects, that can potentially help to create an energy efficient information technology.
- Only at BESSY II worldwide: IR nanoscopy at very long THz wavelengthsThe team at the IRIS beamline at BESSY II has created a new experimental option: They achieved infrared nanoscopy with a spatial resolution of around 50 nm at very long THz wavelengths. This was possible thanks to a temporal pattern of light pulses known as the low-alpha operating mode at BESSY II. Worldwide, BESSY II is the only synchrotron light source at which users could perform nanoscopy in a single setup from 25 to 4000 cm-1, a unique opportunity for ultra-broadband characterisation of complex materials at the nanoscale in both the life sciences and materials sciences.
- Ultrafast demagnetisation - Thinner iron, stronger effectThe thinner an iron film, the more easily it can be demagnetised by a laser pulse. Researchers at the University of Duisburg-Essen, working with Helmholtz-Zentrum Berlin and other partners, have discovered why: the key lies in the magnetic order at the material's interfaces. In the long term, these findings could contribute to the development of new technologies for magnetic data storage. The results have been published in the scientific journal Advanced Science.