  Alvarez Ferrero, G.; Åvall, G.; Mazzio, K.A.; Son, Y.; Janßen, K.; Risse, S.; Adelhelm, P.: Co-Intercalation Batteries (CoIBs): Role of TiS₂ as Electrode for Storing Solvated Na Ions. Advanced Energy Materials 12 (2022), p. 2202377/1-11

10.1002/aenm.202202377
Open Access Version

Abstract:
The co-intercalation of solvent molecules along with Na+ into the crystal lattice of electrode materials is an undesired process in sodium batteries. An exception is the intercalation of ether solvated alkali ions into graphite, a fast and highly reversible process. Here, reversible co-intercalation is shown to also be possible for other layered materials, namely titanium disulfide. Operando X-ray diffraction and dilatometry are used to demonstrate different storage mechanisms for different electrolyte solvents. Diglyme is found to co-intercalate into the TiS2 leading to a change in the voltage profile and an increase in the interlayer spacing (≈150%). This behavior is different compared to other solvents, which expand much less during Na storage (24% for tetrahydrofuran [THF] and for a carbonate mixture). For all solvents, specific capacities (2nd cycle) exceed 250 mAh g−1 whereas THF exhibited the best stability after 100 cycles. The solvent co-intercalation is rationalized by density functional theory and linked to the stability of the solvation shells, which is largest for diglyme. Finally, the TiS2 electrode with diglyme electrolyte is paired with a graphite electrode to realize the first proof-of-concept solvent co-intercalation battery, that is, a battery with two electrodes that both rely on reversible co-intercalation of solvent molecules.