Seeger, J.; Ivanova, M.E.; Meulenberg, W.A.; Sebold, D.; Stöver, D.; Scherb, T.; Schumacher, G.; Escolastico, S.; Solis, C.; Serra, J.M.: Synthesis and Characterization of Nonsubstituted and Substituted Proton-Conducting La1-xWO12-y. Inorganic Chemistry 52 (2013), p. 10375-10386
10.1021/ic401104m
Abstract:
Mixed proton−electron conductors (MPEC) can be used as gas separation membranes to extract hydrogen from a gas stream, for example, in a power plant. From the different MPEC, the ceramic material lanthanum tungstate presents an important mixed protonic−electronic conductivity. Lanthanum tungstate La6−xWO12−y (with y = 1.5x + δ and x = 0.5−0.8) compounds were prepared with La/W ratios between 4.8 and 6.0 and sintered at temperatures between 1300 and 1500 °C in order to study the dependence of the single-phase formation region on the La/W ratio and temperature. Furthermore, compounds substituted in the La or W position were prepared. Ce, Nd, Tb, and Y were used for partial substitution at the La site, while Ir, Re, and Mo were applied for W substitution. All substituents were applied in different concentrations. The electrical conductivity of nonsubstituted La6−xWO12−y and for all substituted La6−xWO12−y compounds was measured in the temperature range of 400−900 °C in wet (2.5% H2O) and dry mixtures of 4% H2 in Ar. The greatest improvement in the electrical characteristics was found in the case of 20 mol % substitution with both Re and Mo. After treatment in 100% H2 at 800 °C, the compounds remained unchanged as confirmed with XRD, Raman, and SEM.