Spintronics: Resetting the future of Heat Assisted Magnetic Recording

The nanostructured membrane has a honeycomb pattern with nanoholes of 68 nm in diameter. The nanoholes pin down the magnetic domains.

The nanostructured membrane has a honeycomb pattern with nanoholes of 68 nm in diameter. The nanoholes pin down the magnetic domains. © HZB

A thin film of Dysprosium-Cobalt (green) has been sputtered on top of the membrane, resulting in an array of antidots. The magnetic moments of DyCo<sub>5</sub> are perpendicular to the plane and stable against external magnetic fields. A laser pulse can be used to locally increase the temperature of individual bits.

A thin film of Dysprosium-Cobalt (green) has been sputtered on top of the membrane, resulting in an array of antidots. The magnetic moments of DyCo5 are perpendicular to the plane and stable against external magnetic fields. A laser pulse can be used to locally increase the temperature of individual bits. © HZB

Moderate heating up to 80 &deg;Celsius does tilt the magnetic moment associated to a single bit into the plane. Upon cooling to room temperature, the magnetic moment stays in plane, until it is overwritten by a magnetic writing head.

Moderate heating up to 80 °Celsius does tilt the magnetic moment associated to a single bit into the plane. Upon cooling to room temperature, the magnetic moment stays in plane, until it is overwritten by a magnetic writing head. © HZB

A HZB team has examined thin films of Dysprosium-Cobalt sputtered onto a nanostructured membrane at BESSY II. They showed that new patterns of magnetization could be written in a quick and easy manner after warming the sample to only 80 °Celsius, which is a much lower temperature as compared to conventional Heat Assisted Magnetic Recording systems. This paves the way to fast and energy efficient ultrahigh density data storage. The results are published now in the new journal Physical Review Applied.

To increase data density further in storage media, materials systems with stable magnetic domains on the nanoscale are needed. For overwriting a specific nanoscopic region with new information, a laser is used to heat locally the bit close to the so called Curie-Temperature, typically several hundred degrees Celsius. Upon cooling, the magnetic domain in this region can be reoriented in a small external magnetic field, known as Heat Assisted Magnetic Recording (HAMR). In industry, Iron-Platinum materials are currently used as magnetic media for the development of such HAMR-data storage devices.

Magnetic signals mapped at BESSY II before and after heating

A HZB team has now examined a new storage media system of Dysprosium and Cobalt, which shows key advantages with respect to conventional HAMR materials: A much lower writing temperature, a higher stability of the magnetic bits, and a versatile control of the spin orientation within individual magnetic bits. They achieved this by sputtering a thin film of Dysprosium and Cobalt onto a nanostructured membrane. The membrane was produced by scientific cooperation partners at the Institute of Materials Science of Madrid. The system shows a honeycomb antidot pattern with distances of 105 nanometers between nanoholes, which are 68 nanometers in diameter. These nanoholes act themselves as pinning centers for stabilizing magnetic wall displacements. The magnetic moments of DyCo5 are perpendicular to the plane and stable against external magnetic fields.

Energy efficient process

HZB-physicist Dr. Jaime Sánchez-Barriga and his team could demonstrate that warming the system to only 80 degrees Celsius is sufficient to tilt the magnetic moments in the DyCo5 film parallel to the surface plane. With measurements at the PEEM and XMCD instruments at BESSY II they could map precisely the magnetic signals before, during and after warming. After cooling to room temperature it is then easy to reorient the magnetic domains with a writing head and to encode new information. “This process in DyCo5 is energy efficient and very fast”, states Dr. Florin Radu, co-author of the study. “Our results show that there are alternative candidates for ultrahigh density HAMR storage systems, which need less energy and promise other important advantages as well”, adds Sánchez-Barriga.

Publication: Ferrimagnetic DyCo5 nanostructures for bits in heat-assisted magnetic recording.  A. A. Ünal, S. Valencia, F.  Radu, D. Marchenko, K. J. Merazzo, M. Vázquez, and J. Sánchez-Barriga, Phys. Rev. Applied 5, 064007
Doi: http://dx.doi.org/10.1103/PhysRevApplied.5.064007

arö

You might also be interested in

  • 8th World Conference on PV Energy Conversion
    News
    19.09.2022
    8th World Conference on PV Energy Conversion
    The WCPEC-8 woll take place from 26 – 30 September 2022 in the Milano Convention Centre in Milan, Italy.
    Also scientists from PVcomB will present latest results about their research work to photovoltaics.

  • 40 years of research with synchrotron light in Berlin
    News
    14.09.2022
    40 years of research with synchrotron light in Berlin
    Press release _ Berlin, 14 September: For decades, science in Berlin has been an important driver of innovation and progress. Creative, talented people from all over the world come together here and develop new ideas from which we all benefit as a society. Many discoveries – from fundamental insights to marketable products – are made by doing research with synchrotron light. Researchers have had access to this intense light in Berlin for 40 years. It inspires many scientific disciplines and is an advantage for Germany.

  • New road towards spin-polarised currents
    Science Highlight
    08.09.2022
    New road towards spin-polarised currents
    The transition metal dichalcogenide (TMD) series are a family of promising candidate materials for spintronics. A study at lightsource BESSY II has unveiled that in one of those materials even simple linear polarised light is sufficient to selectively manipulate spins of different orientations. This result provides an entirely new route for the generation of spin-polarised currents and is a milestone for the development of spintronic and opto-spintronic devices.