Nanodiamonds can be activated as photocatalysts with sunlight
The illustration shows two variants of nanodiamond materials with different surfaces: C230H106 on the left, C286H68 on the right. Sp3 C atoms (diamond) black, sp3x C atoms (fullerene-like) brown, H atoms: Light grey. When the surface is partially covered by hydrogen atoms, nanodiamonds can absorb light in the visible range and emit electrons into solution. © T. Kirschbaum / HZB
Nanodiamond materials have potential as low-cost photocatalysts. But until now, such carbon nanoparticles required high-energy UV light to become active. The DIACAT consortium has therefore produced and analysed variations of nanodiamond materials. The work shows: If the surface of the nanoparticles is occupied by sufficient hydrogen atoms, even the weaker energy of blue sunlight is sufficient for excitation. Future photocatalysts based on nanodiamonds might be able to convert CO2 or N2 into hydrocarbons or ammonia with sunlight.
Nanodiamond materials have great potential as catalysts. Inexpensive nanoparticles made of carbon provide very large surfaces compared to their volume. However, to catalytically accelerate chemical reactions in an aqueous medium, electrons from the catalyst need to go into solvation and this requires in pure diamond materials high-energy UV light for excitation. On the other hand, the extremely small sizes of the nanoparticles allow new molecular states on the surfaces of nanodiamonds that also absorb visible light.
Different surfaces
As part of the DIACAT project, a team at HZB has now investigated different variants of nanodiamond materials during excitation with light and analysed the processes with extremely high time resolution. Nanodiamond samples with different surface chemistries were produced by the group of Dr. Jean-Charles Arnault, CEA, France and Prof. Anke Krueger, now at the University of Stuttgart. The nanoparticles differed in their surfaces, which contained different amounts of hydrogen or oxygen atoms.
Hydrogen helps - and fullerene-like carbon too
"The hydrogen on the surfaces makes electron emission much easier," explains Dr Tristan Petit, nanodiamond expert at HZB. "Among the many variants, we discovered that a certain combination of hydrogen as well as fullerene-like carbon on the surfaces of the nanoparticles is ideal," he says.
Ultrafast laser excitations
In the ULLAS femtosecond laser facility at HZB they studied aqueous nanodiamond dispersions with different surface terminations such as hydrogen, -OH or -COOH after exciting them with ultrafast laser pulses. “We were able to experimentally measure exactly how the absorption profile behaves with different excitation wavelengths in the UV range at 225 nm and with blue light in the visible range at 400 nm”, explains Dr Christoph Merschjann, HZB.
Picoseconds after the excitation
"We wanted to find out what happens in the first crucial picoseconds after excitation with light, because that is the time when an electron leaves the surface and goes into the water," says Merschjann. The theory team led by Dr Annika Bande contributed modelling with density functional theory to interpret the spectra. The data showed, as expected, that UV light brings electrons into solution in all samples, but for those samples that had fullerene-like carbon on their surfaces, this was also achieved with visible light.
Blue light can work
"In this work we show - to the best of our knowledge for the first time - that the emission of solvated electrons from nanodiamonds in water is possible with visible light!", Petit summarises the results. This is a decisive step towards opening up nanodiamond materials as photocatalysts. These inexpensive and metal-free materials could be a key to further processing CO2 into valuable hydrocarbons with sunlight in the future, or even to convert N2 into ammonia.
Note: DIACAT has received funding from the European Union's Horizon 2020 Research and Innovation Programme under Grant Agreement no 665085.
- Thin nickel films boost green hydrogen productionUltra-thin nickel oxide coatings can significantly improve the performance of anion exchange membrane (AEM) water electrolysers, a promising technology for producing green hydrogen. This was demonstrated by a team led by HZB scientist Dr. Michelle Browne. The results show that a nickel oxide film only 10 nanometres thick outperformed conventional nickel oxide powder electrodes while using less than 1% of the catalyst material. The study is published in the Journal of Materials Chemistry A,
- Detailed insights at BESSY II into the oxidation processes of copperBefore pure copper oxide builds up, complex superstructures such as ‘29’CuxO, are formed. The new results on the '29' CuxO superstructure have relevance for catalyst research and corrosion protection in the development of safe copper containers for nuclear waste repositories.
- BESSY II: Evaporated perovskites in tandem solar cells improvedPerovskite-silicon tandem solar cells achieve significantly higher efficiencies than silicon solar cells on their own. One particularly attractive method is co-evaporation of the perovskite precursor molecules on top of the silicon subcell. Scientists at HZB have analysed film growth on the nanoscale at BESSY II and found a new way to improve the quality of the perovskite layer: adding a thin seed layer of caesium chloride between the two sub-cells promotes uniform perovskite growth and suppresses the formation of undesired lead iodide at the interface.