A simpler way to inorganic perovskite solar cells

Under the scanning electron microscope, the CsPbI<sub>3</sub> layer (large blocks in the upper part of the image) on the FTO substrate looks almost exactly the same after annealing in ambient air as after annealing under controlled conditions.

Under the scanning electron microscope, the CsPbI3 layer (large blocks in the upper part of the image) on the FTO substrate looks almost exactly the same after annealing in ambient air as after annealing under controlled conditions. © HZB

Die Box-Chart-Statistik zeigt Wirkungsgrade von Solarzellen, die unter kontrollierten Bedingungen hergestellt wurden im Vergleich mit Solarzellen, die in Umgebungsluft gegl&uuml;ht wurden. &nbsp;

Die Box-Chart-Statistik zeigt Wirkungsgrade von Solarzellen, die unter kontrollierten Bedingungen hergestellt wurden im Vergleich mit Solarzellen, die in Umgebungsluft geglüht wurden.   © HZB

Inorganic perovskite solar cells made of CsPbI3 are stable over the long term and achieve good efficiencies. A team led by Prof. Antonio Abate has now analysed surfaces and interfaces of CsPbI3 films, produced under different conditions, at BESSY II. The results show that annealing in ambient air does not have an adverse effect on the optoelectronic properties of the semiconductor film, but actually results in fewer defects. This could further simplify the mass production of inorganic perovskite solar cells.

Metal halide perovskites have optoelectronic properties that are ideally suited for photovoltaics and optoelectronics. When they were discovered in 2009, halide perovskites in solar cells achieved an efficiency of 3.9 per cent, which then increased extremely fast. Today, the best perovskite solar cells achieve efficiencies of more than 26 per cent. However, the best perovskite semiconductors contain organic cations such as methylammonium, which cannot tolerate high temperatures and humidity, so their long-term stability is still a challenge. However, methylammonium can be replaced by inorganic cations such as Cesium (Cs). Inorganic halide perovskites with the molecular formula CsPbX3 (where X stands for a halide such as chloride, bromide and iodide) remain stable even at temperatures above 300 °C. CsPbI3 has the best optical properties for photovoltaics (band gap 1.7 eV).

Production in glove boxes

Perovskite semiconductors are produced by spin coating or printing from a solution onto a substrate and are typically processed in glove boxes under a controlled atmosphere: There, the solvent is evaporated by heating, after which a thin layer of perovskite crystallizes. This 'controlled environment' significantly increases the cost and complexity of production.

...or ambient conditions

In fact, CsPbI3 layers can also be annealed under ambient conditions without loss or even with an increase in efficiency of up to 19.8 per cent, which is even better than samples annealed under controlled conditions.

What happens at the interfaces?

"We investigated the interfaces between CsPbI3 and the adjacent material in detail using a range of methods, from scanning electron microscopy to photoluminescence techniques and photoemission spectroscopy at BESSY II," says Dr. Zafar Iqbal, first author and postdoctoral researcher in Antonio Abate's team.

BESSY II unveils a surface modification

At BESSY II, the team of Prof. Marcus Bär used hard X-ray photoelectron spectroscopy (HAXPES) to analyse the chemical and electronic structure of the differently annealed CsPbI3 and perovskite/hole transport layer interfaces. "In the samples that were annealed in ambient air, we observed a surface modification that improves the mobility of the charge carriers at the interface," explains Iqbal. Optical spectroscopy showed that annealing in air resulted in fewer defects.

Upscaling might become simpler

"Our study explains why the annealing of CsPbI3 films in ambient air works well," says Iqbal. This could be particularly interesting for upscaling processes for potential mass production.

Note: Zafar Iqbal was financed by a fellowship by Deutscher Akademischer Austauschdienst (DAAD) during his PhD in the Abate Group.

arö

  • Copy link

You might also be interested in

  • HZB patent for semiconductor characterisation goes into serial production
    News
    10.10.2024
    HZB patent for semiconductor characterisation goes into serial production
    An HZB team has developed an innovative monochromator that is now being produced and marketed by a company. The device makes it possible to quickly and continuously measure the optoelectronic properties of semiconductor materials with high precision over a broad spectral range from the near infrared to the deep ultraviolet. Stray light is efficiently suppressed. This innovation is of interest for the development of new materials and can also be used to better control industrial processes.
  • Photovoltaic living lab reaches the 100 Megawatt-hour mark
    News
    27.09.2024
    Photovoltaic living lab reaches the 100 Megawatt-hour mark
    About three years ago, the living laboratory at HZB went into operation. Since then, the photovoltaic facade has been generating electricity from sunlight. On September 27, 2024, it reached the milestone of 100 megawatt-hours.

  • Alternating currents for alternative computing with magnets
    Science Highlight
    26.09.2024
    Alternating currents for alternative computing with magnets
    A new study conducted at the University of Vienna, the Max Planck Institute for Intelligent Systems in Stuttgart, and the Helmholtz Centers in Berlin and Dresden takes an important step in the challenge to miniaturize computing devices and to make them more energy-efficient. The work published in the renowned scientific journal Science Advances opens up new possibilities for creating reprogrammable magnonic circuits by exciting spin waves by alternating currents and redirecting these waves on demand. The experiments were carried out at the Maxymus beamline at BESSY II.