Bergner, F.; Ulbricht, A.; Lindner, P.; Keiderling, U.; Malerba, L.: Post-irradiation annealing behavior of neutron-irradiated FeCu, FeMnNi and FeMnNiCu model alloys investigated by means of small-angle neutron scattering. Journal of Nuclear Materials 454 (2014), p. 22-27
10.1016/j.jnucmat.2014.07.038

Abstract:
Neutron irradiation of reactor pressure vessel steels gives rise to the formation of thermodynamically stable and unstable nano-features. The present work is focused on the stability of Cu-, Mn- and Ni-containing solute clusters in model alloys exposed to post-irradiation annealing. Fe0.1Cu, Fe1.2Mn0.7Ni and Fe1.2Mn0.7Ni0.1Cu (wt%) model alloys irradiated up to neutron exposures of 0.1 and 0.19 dpa (displacements per atom) were annealed at stepwise increasing temperatures in the range from 300 °C (i.e. near irradiation temperature) to 500 °C and characterized by means of small-angle neutron scattering (SANS). We have found characteristic differences in the annealing behavior of the alloys. In particular, there is a non-trivial (synergistic–antagonistic) interplay of Mn/Ni and Cu.